Preparation, characterization and magneto-optical investigations of electrodeposited Co/Au films

Au/Co(4–8ML)/Au single magnetic layers and Au(8ML)/Co(4ML)/Au(8ML)/Co(8ML)/Au bilayer were sequentially grown by electrodeposition on an Au(111) buffer layer electrodeposited on Si(111). The technique used in this work provides full control on the structure and the chemical composition of the different layers (no alloying) as well as on the chemistry at interfaces. scanning tunneling microscopy (STM) and atomic force microscopy (AFM) imaging and X-ray diffraction measurements show that atomically flat continuous Co(0001) layers (4–8ML) can be grown in epitaxy with the Au(111) substrate and that the 2nm-thick spacer is also a continuous Au(111) layer. The Co ultrathin layers (4 and 8ML) exhibit perpendicular magnetic anisotropy. The lateral magnetic homogeneity and magnetization reversal process have been investigated by scanning magneto-optical Kerr effect (MOKE) magnetometry and global Kerr microscopy. The correlation between magnetization switching behaviour in each layer of the Co-bilayer stack has been evidenced from in-depth sensitive MOKE measurements and microscopy. The strong coupling observed between the two Co layers is attributed to magnetostatic interaction at domain wall boundaries.