Production of high porosity nanoparticles of cerium oxide in clay
Microporous and Mesoporous Materials(2007)
Abstract
Cerium oxide nanoparticles modified montmorillonite was obtained by interaction of a clay with (NH4)2Ce(NO3)6. The mean size of cerium oxide nanoparticles in clay was at 3.5nm. The product was an amorphous solid and showed high permanent porosity and stability at high temperatures. The amorphous structure of the sample was proven by X-ray diffraction and electronic diffraction. The porous structure was studied by means of chemisorption and it was shown that samples calcined at 550°C had SBET=239m2/g; micropore volume=0.1839cm3/g; average pore diameter=3.07nm.
MoreTranslated text
Key words
Nanocomposite,Stabilized nanoparticles,Cerium oxide nanoparticles,Clay,Montmorillonite
AI Read Science
Must-Reading Tree
Example
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
Generate MRT to find the research sequence of this paper
Chat Paper
Summary is being generated by the instructions you defined