Critical Current Densities and Magnetic Hysteresis Losses in Submicron Filament Bronze-Processed Nb/sub 3/sn Wires
IEEE Transactions on Magnetics(1991)
摘要
Submicron-filament bronze-processed multifilamentary Nb/sub 3/Sn wires with Cu-5at%Sn-X (X: Mn, Ni, Si, Ge, B, P, Zn, Al) ternary alloy matrix and Nb-1at.%Ta alloy cores were fabricated. The cross-sectional structure of wires was the central-Cu-stabilizer type to facilitate, by external Sn diffusion, improvements in critical current density and hysteresis losses. The Nb-1Ta core decreased the hysteresis loss in spite of the increase of the critical current densities. By the addition of Zn, Al, the critical current densities and the hysteresis losses were improved. Although hysteresis losses were not decreased by Sn plating, the critical current densities were apparently improved at relatively low temperature heat treatment.< >
更多查看译文
关键词
composite superconductors,critical current density (superconductivity),losses,magnetic hysteresis,niobium alloys,tin alloys,type II superconductors,Cu-Sn matrix,Nb alloy cores,Nb core,Nb-Hf,Nb-Ta,Nb-Ti,Nb-Zr,Nb3Sn,Nb3Sn-CuSn,bronze-processed Nb3Sn wires,critical current density,external Sn diffusion method,low AC loss wire,magnetic hysteresis losses,multifilamentary wires,optimum heat treatment,submicron filament
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要