Porous and strong bioactive glass (13–93) scaffolds fabricated by freeze extrusion technique
Materials Science and Engineering: C(2011)
Abstract
Scaffolds fabricated by current methods often lack the combination of high strength and high porosity for skeletal substitution of load-bearing bones. In this work, freeze extrusion fabrication (FEF), a solid freeform fabrication technique, was investigated for the creation of porous and strong bioactive glass (13–93) scaffolds for potential applications in the repair of loaded bone. The process parameters for forming three-dimensional (3D) scaffolds with a pre-designed, grid-like microstructure by FEF were determined. Following thermal treatment of the as-formed constructs at temperatures up to 700°C, scaffolds consisting of dense glass struts and interconnecting pores (porosity≈50%; pore width≈300μm) were obtained. These scaffolds showed an elastic mechanical response in compression, with a compressive strength of 140±70MPa and an elastic modulus of 5.5±0.5GPa, comparable to the values for human cortical bone. The scaffolds supported the proliferation of osteogenic cells in vitro, showing their biocompatibility. These results indicate that 13–93 bioactive glass scaffolds created by the FEF method could have potential application in the repair and regeneration of load-bearing bones.
MoreTranslated text
Key words
Bioactive glass,Scaffold,Solid freeform fabrication,Freeze extrusion fabrication,Bone repair
AI Read Science
Must-Reading Tree
Example
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
Generate MRT to find the research sequence of this paper
Chat Paper
Summary is being generated by the instructions you defined