Formation of thin boron nitride coating on multiwall carbon nanotube surfaces

Thin boron nitride films were deposited onto outer surfaces of multiwall carbon nanotubes (MWCNTs) by dip coating, which involves infiltration by boric acid solutions and subsequent nitridation of the boron oxide in ammonia flow at 1050°C. The overall composition of the samples was determined by electron energy loss (EELS) and X-ray photoelectron spectroscopy (XPS), the surface composition and chemical structure of the BN coatings by XPS, the morphology of the BN/MWCNT composites by scanning and transmission electron microscopy (SEM, TEM), and the resistance against oxidation at elevated temperatures by thermal analysis (TGA). It was proved that single and multilayer BN coverage were achieved at the applied experimental conditions, and the coated samples showed significantly increased oxidation resistance compared to the uncoated MWCNTs.