Enhanced piezoelectric properties of (Na0.53K0.47)(Nb1−xTax)O3 ceramics by Ta substitution
Ceramics International(2012)
摘要
The effects of Ta substitution for B-site Nb in (Na0.53K0.47)(Nb1−xTax)O3 (NKNT) ceramics were investigated in the range of x=0–0.6. It was found that polymorphic phase transitions (PPT) were significantly influenced by Ta substitution. Transitions among orthorhombic, tetragonal, and cubic phases in sequence with temperature, TO-T and TC, respectively, decreased linearly with x. At x=0.45, TO-T was reduced to room temperature from 182°C at x=0, and subsequently piezoelectric coefficient (d33) at room temperature was enhanced up to 284pC/N from 120pC/N at x=0 due to the coexistence of ferroelectric orthorhombic and tetragonal NKNT phases. With x further increasing beyond x=0.45, d33 decreased due to there being no orthorhombic but only a tetragonal NKNT phase at room temperature with TO-T below room temperature.
更多查看译文
关键词
C. Dielectric properties,C. Piezoelectric properties,NKNT,Polymorphic phase transition
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要