Effect of Cooling Rate on Morphology and Crystallography of Lath Martensite in Fe-Ni Alloys
Materials Science Forum(2010)
摘要
The development of blocks and subblocks in the lath martensite was observed with SEM/EBSD and TEM/Kikuchi diffraction patterns analyses. Morphology of lath martensite formed below Ms temperature was observed using step quenching method in 18 mass% Ni maraging steel. The development of lath martensite structure can be described as follow; lath groups with single K-S variant start to form at the austenite grain boundary. Next, other sub-blocks appear adjacent to the lath groups formed first and these lath groups form macroscopic blocks observed in optical microscopy The morphologies of the lath martensite in Fe -23 mass% Ni alloy cooled at different cooling rates after austenitization were also observed The packet size and block thickness decreases with increasing cooling rate, although the sub-block thickness do not change. A packet locally contains small packets with different relationship of close packed planes, and the amount of small packets increases with increasing the cooling rate.
更多查看译文
关键词
Steels,Lath martensite,Morphology and crystallography,SEM/EBSD
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要