Synthesis, characterization and properties of carbon nanotubes microspheres from pyrolysis of polypropylene and maleated polypropylene

Microspheres assembled from carbon nanotubes (MCNTs), with the diameters ranging from 5.5 to 7.5μm, were synthesized by means of pyrolysis of polypropylene and maleated polypropylene in an autoclave. The characterization of structure and morphology was carried out by X-ray diffractometer (XRD), field-emission scanning electron microscopy (FESEM), (high resolution) transmission electron microscope [(HR)TEM)], selected-area electron diffraction (SAED) and Raman spectrum. As a typical morphology, the possible growth process of MCNTs was also investigated and discussed. The results of nitrogen adsorption–desorption indicate that the Brunauer–Emett–Teller (BET) surface area (140.6m2/g) of the MCNTs obtained at 600°C is about twice as that (74.5m2/g) of carbon nanotubes obtained at 700°C. The results of catalytic experiment show that MCNTs based catalyst has higher catalytic activity than the carbon nanotubes based catalyst for the preparation of methanol and dimethoxy-ethane by oxidation of dimethyl ether.